OEM China Glass Mat Laminated Sheets - DF350A Modified Diphenyl Ether Glass Cloth Rigid Laminated sheet – D&F
OEM China Glass Mat Laminated Sheets - DF350A Modified Diphenyl Ether Glass Cloth Rigid Laminated sheet – D&F Detail:
DF350A consists of woven glass cloth impregnated with a modified diphenyl ether thermosetting resin, laminated under high temperature and pressure. The woven glass cloth shall be alkali-free and treated by KH560.
DF350A possesses good heat resistance, excellent mechanical and dielectric properties, suitable for applications in H-class electric motors or electrical equipment as insulation structural parts or components. Especially used in these electric motors or electrical equipment which require a higher mechanical performances under thermal state stress.
Available thickness: 0.5mm~200mm
Available sheet size:
1500mm*3000mm、1220mm*3000mm、1020mm*2040mm,1220mm*2440mm、1000mm*2000mm and other negotiated sizes.
The Nominal Thickness And Allowed Tolerance (mm)
| Nominal thickness | Deviation | Nominal thickness | Deviation | Nominal thickness | Deviation |
| 0.5 | +/-0.15 | 3 | +/-0.37 | 16 | +/-1.12 |
| 0.6 | +/-0.15 | 4 | +/-0.45 | 20 | +/-1.30 |
| 0.8 | +/-0.18 | 5 | +/-0.52 | 25 | +/-1.50 |
| 1 | +/-0.18 | 6 | +/-0.60 | 30 | +/-1.70 |
| 1.2 | +/-0.21 | 8 | +/-0.72 | 35 | +/-1.95 |
| 1.5 | +/-0.25 | 10 | +/-0.94 | 40 | +/-2.10 |
| 2 | +/-0.30 | 12 | +/-0.94 | 45 | +/-2.45 |
| 2.5 | +/-0.33 | 14 | +/-1.02 | 50 | +/-2.60 |
Bending Deflection (mm)
|
Thickness |
Bending deflection |
|
|
1000（Ruler length） |
500（Ruler length） |
|
|
3.0～6.0 |
≤10 |
≤2.5 |
|
6.1～8.0 |
≤8 |
≤2.0 |
|
＞8.0 |
≤6 |
≤1.5 |
Physical, Mechanical And Dielectric Properties
| No. | Properties | Unit | Standard value | Typical value | ||
| 1 | Density | g/cm3 | 1.70～1.95 | 1.9 | ||
| 2 | Flexural strength, perpendicular to laminations (Lengthwise) | At normal condition | MPa | ≥400 | 540 | |
| 180℃+/-2℃ | ≥200 | 400 | ||||
| 3 | Impact strength（Charpy, notch, lengthwise) | kJ/m2 | ≥37 | 50 | ||
| 4 | Adhesive/bond strength | N | ≥5000 | 6900 | ||
| 5 | Water absorption | mg | See next table | 11.8 | ||
| 6 | Insulation resistance, parallel to laminations | At normal condition | MΩ | ≥1.0 x 106 | 5.3 x 107 | |
| After 24h in water | ≥1.0 x 102 | 3.8 x 104 | ||||
| 7 | Dielectric dissipation factor 1MHz | – | ≤0.05 | 1.03 x 10-2 | ||
| 8 | Dielectric constant 1MHz | – | ≤5.5 | 4.7 | ||
| 9 | Breakdown voltage，parallel to laminations ( in transformer oil at 90℃+/-2℃) | kV | ≥30 | 35 | ||
| 10 | Dielectric Strength，perpendicular to laminations ( in transformer oil at 90℃+/-2℃),2mm sheet | MV/m | ≥11.8 | 18 | ||
Water Absorption
|
Average thickness of test samples (mm) |
Water absorption (mg) |
Average thickness of test samples (mm) |
Water absorption (mg) |
Average thickness of test samples (mm) |
Water absorption (mg) |
|
0.5 |
≤17 |
2.5 |
≤21 |
12 |
≤38 |
|
0.8 |
≤18 |
3.0 |
≤22 |
16 |
≤46 |
|
1.0 |
≤18 |
5.0 |
≤25 |
20 |
≤52 |
|
1.6 |
≤19 |
8.0 |
≤31 |
25 |
≤61 |
|
2.0 |
≤20 |
10 |
≤34 |
See Remarks 2 |
≤73 |
| Remarks:1) If the calculated average of measured thickness is between two thickness mentioned in this table, the values will be acquired by interpolation. If the caculated average of measured thickness is less 0.5mm, the vales will not be over 17mg. If the caculated average of measured thickness is over 25mm, the value will not be over 61mg.2) If nominal thickkness is more than 25mm,it shall be machined to 22.5mm on one side. The machined side should be smooth. | |||||
Packing And Storage
The sheets shall be stored in a place where temperature is no higher than 40℃, and be placed horizontally on a bedplate with a height of 50mm or above.
Keep away from fire, heat (heating apparatus) and direct sunshine. The storage life of sheets is 18 months from the date of leaving factory. If the storage duration is over 18 months, the product also could be used after being tested to be qualified.
Remarks and Precautions for Application
A high speed and small cutting depth shall be applied when machining because of sheets’ weak thermal conductivity.
Machining and cutting this product will release much dust and smoke. Suitable measures should be taken to ensure dust levels are within acceptable limits during operations. Local exhaust ventilation and using the suitable dust/particle masks are advised.
The sheets are subject to moisture after being machined, a coating of insulating vanish is recommended.
Product detail pictures:
Related Product Guide:
Dependable high-quality and fantastic credit standing are our principles, which will help us at a top-ranking position. Adhering to your tenet of "quality very first, client supreme" for OEM China Glass Mat Laminated Sheets - DF350A Modified Diphenyl Ether Glass Cloth Rigid Laminated sheet – D&F , The product will supply to all over the world, such as: Vietnam, Saudi Arabia, Norwegian, We have exported our products all over the world, especially the USA and European countries. Furthermore, all of our products are manufactured with advanced equipment and strict QC procedures to ensure high quality.If you are interested in any of our products, please don't hesitate to contact us. We will try our best to meet your needs.
By Beryl from Netherlands - 2018.05.22 12:13
The company can keep up with the changes in this industry market, product updates fast and the price is cheap, this is our second cooperation, it's good.
By Julie from Poland - 2018.11.22 12:28
-
Top Suppliers Diphenyl Ether Laminated Glass Cl...
-
OEM Customized Copper Braid Flexible Bus Bar -...
-
Excellent quality Braided Flexible Busbar - Cu...
-
Factory best selling F-Dmd - Custom copper foi...
-
OEM/ODM Supplier Leiterplattenmaterial - China...
-
Hot New Products High Volatge Insulator - DMC/...