China Hot sale Gpo3 Fiberglass Sheet - GPO-3 (UPGM203) Unsaturated Polyester Glass Mat Laminated Sheet – D&F manufacturers and Exporter

Hot sale Gpo3 Fiberglass Sheet - GPO-3 (UPGM203) Unsaturated Polyester Glass Mat Laminated Sheet – D&F

short description:

Product Detail

Product Tags

Feedback (2)

Our company since its inception, constantly regards product or service high quality as business life, continually improve creation technology, make improvements to product high-quality and consistently strengthen business total high-quality management, in strict accordance together with the national standard ISO 9001:2000 for D279 Epoxy Impregnated Dmd, melamine fiberglass cloth sheet, Laminated Bus Bar Manufacturer, We are looking forward to cooperating with all customers from at home and abroad. Moreover, customer satisfaction is our eternal pursuit.

Hot sale Gpo3 Fiberglass Sheet - GPO-3 (UPGM203) Unsaturated Polyester Glass Mat Laminated Sheet – D&F Detail:

GPO-3 Molded Sheet (also called GPO3,UPGM203) consists of alkali–free glass mat impregnated and bonded with the unsaturated polyester resin, and laminated under high temperature and high pressure in mould. It has good machinability, high mechanical strength, good dielectric properties, excellent proof tracking resistance and arc resistance. It is with UL certification and passed the test of REACH and RoHS, etc. It is also called as GPO-3 or GPO3 sheet,GPO-3 or GPO3 insulation board.

It is applicable for making insulation structural and supportive components or parts in F-class electric motors, transformers, switch gears, circuit breakers and electrical equipment. The UPGM can be directly molded into different profiles or insulation structural parts.

Thickness range：2mm—60mm

Sheet size：1020mm *2010mm, 1000mm*2000mm, 1220mm*2440mm and other negotiated thickness or/and sizes

Main color: red, white or other negotiated colors

Besides the UPGM laminated sheets, we also produce and supply the EPGM 203 sheets, the sheet dimension are the same as those of GPO-3. The color is yellowish or green. Please contact me for more information.

GPO-3 UPGM203(1)
GPO-3 (2)

Technical Requirements

Appearance

Its surface shall be flat and smooth, free from blisters, wrinkles or cracks and reasonably free from other small imperfections such as scratches, dents and uneven colors.

Normal thickness and tolerance

Nominal Thickness (mm)	Allowed tolerance (mm)	Nominal Thickness (mm)	Allowed tolerance (mm)
0.8	+/-0.23	12	+/-0.90
1.0	+/-0.23	14	+/-1.00
2.0	+/-0.30	16	+/-1.10
3.0	+/-0.35	20	+/-1.30
4.0	+/-0.40	25	+/-1.40
5.0	+/-0.55	30	+/-1.45
6.0	+/-0.60	40	+/-1.55
8.0	+/-0.70	50	+/-1.75
10.0	+/-0.80	60	+/-1.90
Note: For sheets of non-nominal thickness not listed in this table, the allowed deviation shall be the same as that of the next greater thickness.

Physical, mechanical and electrical properties

Properties			Unit	Standard value	Typical value	Test method
Density			g/cm3	1.65~1.95	1.8	GB/T 1033.1-2008
						(method A)
Water absorption, 3mm thickness			%	≤ 0.2	0.16	ASTM D790-03
Flexural strength,perpendicular to laminations (Lengthwise)		At normal condition	MPa	≥180	235	ASTM D790-03
		130℃+/-2℃		≥100	144
Flexural modulus, perpendicular to laminations (Lengthwise)		At normal condition	MPa	-	1.43 x 104
		130℃+/-2℃		-	1.10 x 104
Flexural strength,perpendicular to laminations (Lengthwise)		Lengthwise	MPa	≥170	243	GB/T 1449-2005
		Crosswise		≥150	240
Impact Strength, parallel to laminations			KJ/m2	≥40	83.1	GB/T 1043.1-2008
(Charpy, unnotched)
Impact Strength, parallel to laminations			J/m	-	921	ASTM D256-06
(Izod, notched)
Tensile strength			MPa	≥150	165	GB/T 1040.2-2006
Tensile elasticity modulus			MPa	≥1.5×104	1.7 x 104
Tensile strength,parallel to laminations	Lengthwise		MPa	≥55	165	GB/T1447-2005
	Crosswise			≥55	168
	Perpendicular to laminations		MPa	-	230	ASTM D695-10
Compression strength

Dielectric strength,perpendicular to laminations (in 25# transformer oil at 90℃+/-2℃,short-time test, Φ25mm/Φ75mm cylindrical electrode )			KV/mm	≥12	135	IEC60243-1:2013
Breakdown voltage,parallel to lanimations (in 25# transformer oil at 90℃+/-2℃,short-time test, Φ130mm/Φ130mm plate electrode )			KV	≥35	＞100
Relative permittivity （1MHz）			-	≤ 4.8	4.54	GB/T 1409-2006
Dielectric dissipation factor （1MHz）			-	≤ 0.03	1.49 x 10-2
Arc Resistance			s	≥180	187	GB/T 1411-2002
Tracking resistance	CTI		V	≥600	CTI 600
					Overpass	GB/T 4207-2012
	PTI			≥600	PTI 600
Insulation resistance	At normal condition		Ω	≥1.0×1013	5.4 x 1014	GB/T 10064-2006
(Taper pin electrodes)	After 24h in water			≥1.0×1012	2.5 x 1014
Flammability (Vertical method)			Grade	V-0	V-0	UL94-2013
Glow wire			-	-	GWIT:960/3.0	GB/T5169.13-2006
Barcol hardness			-	≥ 55	60	ASTM D2583-07

Inspection, Mark, Packaging and Storage

1) Each batch should be tested before dispatch. The inspection items for Routine Test shall include Clause 2.1, 2.2, and Item 1 and Item 3 of Table 6 in Clause 2.3. The items in Clause 2.1, 2.2, should be checked one by one.

2) The sheets shall be stored in a place where temperature is no higher than 40℃, and be placed horizontally on a bed plate with a height of 50mm or above. Keep away from fire, heat (heating apparatus) and direct sunshine. The storage life of sheets is 18 months from the date of leaving factory. If the storage duration is over 18 months, the product also could be used after being tested to be qualified.

Remarks and Precautions for Handling and Use

1)A high speed and small depth of cutting shall be applied when machining because of sheets’ weak thermal conductivity.

2) Machining and cutting this product will release much dust and smoke. Suitable measures should be taken to ensure dust levels are within acceptable limits during operations. Local exhaust ventilation and use of suitable dust/particle masks is advised.