China 3240 Epoxy Phenolic Glass Cloth Base Rigid Laminated Sheet manufacturers and Exporter

3240 Epoxy Phenolic Glass Cloth Base Rigid Laminated Sheet

short description:

3240 Epoxy Phenolic Glass Cloth Base Rigid Laminated Sheet consists of alkali-free woven glass cloth impregnated and bonded with epoxy phenolic thermosetting resin, laminated under high temperature and pressure. With a higher mechanical strength and excellent electrical strength, it is intended for the electric motors or electrical equipment as insulation structural components or parts, even can be used under humid condition or in transformer oil. It also passed toxic and hazardous substance detection (passed REACH &RoHS test). The equivalent type number is PFGC201, Hgw2072 and G3.

Available thickness: 0.5mm~200mm

Available sheet size: 1500mm*3000mm、1220mm*3000mm、1020mm*2040mm,1220mm*2440mm、1000mm*2000mm and other negotiated sizes.

Send email to us

Product Detail

Product Tags

Technical Requirements

1.1 Appearance: the surface of sheet shall be flat and smooth, free of air bubbles, wrinkles or cracks and reasonably free of other small imperfections such as scratches, dents, etc. The edge of sheet shall be tidy and be free of delaminations and cracks. The color shall be substantially uniform, but a few stains are permissible.

1.2 Dimension and allowed tolerance

1.2.1 Width and Length of Sheets

Width & Length (mm)	Tolerance (mm)
＞970～3000	+/-25

1.2.2 The nominal thickness & tolerance

Nominal thickness (mm)

Tolerance (mm)

Nominal thickness (mm)

Tolerance (mm)

0.5

0.6

0.8

1.0

1.2

1.6

2.0

2.5

3.0

4.0

5.0

6.0

8.0

+/-0.12

+/-0.13

+/-0.16

+/-0.18

+/-0.20

+/-0.24

+/-0.28

+/-0.33

+/-0.37

+/-0.45

+/-0.52

+/-0.60

+/-0.72

+/-0.82

+/-0.94

+/-1.02

+/-1.12

+/-1.30

+/-1.50

+/-1.70

+/-1.95

+/-2.10

+/-2.30

+/-2.45

+/-2.50

+/-2.80

Remarks: For the non-nominal thickness not listed in this table, the deviation shall be the same as that of the next greater thickness.

1.3 Bending Deflection

Thickness (mm)

Bending Deflection

1000mm（Ruler length） (mm)

500mm（Ruler length）(mm)

3.0～6.0

＞6.0～8.0

＞8.0

≤10

≤8

≤6

≤2.5

≤2.0

≤1.5

1.4 Mechanical processing: the sheets shall be free of cracks, delaminations and scraps when such machining as sawing, drilling, lathing and milling is applied

1.5 The physical, mechanical and electrcal properties

No.	Properties	Unit	Standard value	Typical value
1	Density	g/cm³	1.7～1.95	1.94
2	Water absoprtion (2mm sheet)	mg	≤20	5.7
3	Flexural strength, perpendicular to laminations	MPa	≥340	417
4	Impact strength (Charpy, notch)	kJ/m²	≥30	50
5	Dielectric dissipation factor 50Hz	---	≤5.5	4.48
6	Dielectric constant 50Hz	---	≤0.04	0.02
7	Insulation resistance ( After 24h in water)	Ω	≥5.0 x10⁸	4.9 x10⁹
8	Dielectric strength, perpendicular to laminationsin transformer oil at 90℃+/-2℃, 1mm sheet	kV/mm	≥14.2	16.8
9	Breakdown Voltage, parallel to laminationsin transformer oil at 90℃+/-2℃	kV	≥35	38

Packing, Transportation and Storage

The sheets shall be stored in a place where temperature is no higher than 40℃, and be placed horizontally on a bedplate with a height of 50mm or above. Keep away from fire, heat (heating apparatus) and direct sunshine. The storage life of sheets is 18 months from the date of leaving factory. If the storage duration is over 18 months, the product also could be used after being tested to be qualified.

Remarks and Precautions for Application

A high speed and small cutting depth g shall be applied when machining because of sheets’ weak thermal conductivity.

Machining and cutting this product will release much dust and smoke. Suitable measures should be taken to ensure dust levels are within acceptable limits during operations. Local exhaust ventilation and using the dust/particle masks are advised.

The sheets are subject to moisture after being machined, a coating of insulating vanish is recommended.